PA NEXT Black Powder

High-toughness, high-density powder for bend-resistant, crack-resistant functional parts with isotropic strength in all directions

Raise3D PA NEXT Black Powder is a next-generation SLS 3D printing material engineered for superior toughness and exceptional isotropic performance. With 4-5x higher elongation at break compared to standard PA12, ultra-high powder flowability, and near-perfect isotropic mechanical properties (XYZ deviation within 1 MPa), PA NEXT is the ideal choice for dynamic load-bearing parts, flex-resistant components, and complex structures requiring multi-directional strength.

Raise3D PA NEXT Black Powder 10kg

Order Now

Benefits

Exceptional toughness
Ultimate isotropy
Superior powder flowability
High reuse rate
Balanced mechanical properties
Easy to print

Applications

Industrial dynamic load-bearing components: pneumatic/hydraulic hose connectors, wear-resistant gears, elastic clips, robotic end-effectors.
Automotive chemical-resistant structural parts: fuel/lubricant line brackets, small load-bearing chassis components, door hinge auxiliaries.
Precision load-bearing structural components: high-strength electronic device brackets, industrial connector housings, automation equipment transmission parts.
Custom tooling and fixtures: new energy battery assembly jigs, 3C product inspection fixtures.
Outdoor/low-temperature accessories: small outdoor mechanical parts, cold-climate precision components.

Material Properties

See more details in Technical Data Sheet.

Property	Testing Method	Typical Values (X-Direction)	Typical Values (Y-Direction)	Typical Values (Z-Direction)
Tensile Strength	ISO 527-2	45 MPa	46 MPa	45 MPa
Elongation at Break	ISO 527-2	36%	35%	30%
Tensile Modulus	ISO 527-2	1590 MPa	1670 MPa	1660 MPa
Flexural Strength	ISO 178	55.1 MPa	53.15 MPa	49.05 MPa
Flexural Modulus	ISO 178	1450 MPa	1530 MPa	1335 MPa
Impact Strength / notched A	ISO 179-2	2.89 kJ/㎡	2.48 kJ/㎡	2.54 kJ/㎡
Unnotched Charpy Impact Strength	ISO 179-2	35.58 kJ/㎡	32.36 kJ/㎡	34.07 kJ/㎡
Shore Hardness D	ISO 868-2003	79.5 D	80 D	80 D
Heat Deflection Temp.@1.8 MPa	ISO 75-2	48.3°C	45.3°C	48°C

Compare SLS Powder Properties

Compare the powder’s properties, and find the one that best meets your requirement.

PA NEXT vs PA12 Differentiation Comparison

Comparison Dimension	PA NEXT	PA12
Core Positioning	High toughness, high density, ultimate isotropy	General purpose, high strength, low warping
Elongation at Break	30-36% (4-5x higher than PA12)	6-9%
Isotropic Performance	XYZ deviation within 1 MPa	XYZ deviation 2-3 MPa
Powder Flowability	Bulk density 0.66 g/cm³ (superior)	Bulk density 0.521 g/cm³
Part Density	1.13 g/cm³ (higher)	1.024 g/cm³
Key Applications	Dynamic load-bearing, bend-resistant, multi-directional stress	General functional parts, small-batch end-use parts