PA NEXT GB Black Powder

High-toughness, high-reusability glass bead reinforced powder for rigid, heat-resistant functional parts with superior cost efficiency

Raise3D PA NEXT GB Black Powder is a next-generation glass bead reinforced SLS 3D printing material engineered for exceptional toughness, industry-leading powder reusability, and outstanding isotropic performance. Combining the high rigidity and thermal stability of glass bead reinforcement with 4-5x higher elongation at break compared to standard PA12 GB, PA NEXT GB achieves a remarkable 3:7 mixing ratio (new powder to recycled powder)—far exceeding the typical 5:5 ratio of conventional glass-filled powders. This makes it the ideal choice for dynamic load-bearing parts, precision structural components, and cost-efficient manufacturing applications.

Raise3D PA NEXT GB Black Powder 10kg

Benefits

Industry-leading reusability: achieves 3:7 mixing ratio (fresh: old)
Exceptional toughness
High rigidity
Outstanding heat resistance
High wear resistance
Low warp rate, compatible with complex structural designs

Applications

High-rigidity structural components: equipment enclosures, mounting brackets, and structural frameworks requiring both strength and toughness
Dynamic load-bearing fixtures: tools, jigs, and replacement parts subject to sustained mechanical stress and flexural loads
Thermal-stress environment components: engine bay parts, high-temperature moving components, and heat-resistant assemblies
Industrial end-use parts: industrial-grade structural supports, assembly connectors, and functional mechanical components
Electrical enclosures and functional mechanical parts: low-to-medium volume custom manufacturing, suitable for applications requiring durable housings and impact resistance
Molds and tooling: suitable for medium-temperature rapid prototyping, simple injection molds, and vacuum forming molds.

Material Properties

See more details in Technical Data Sheet.

Property	Testing Method	Typical Values (X-Direction)	Typical Values (Y-Direction)	Typical Values (Z-Direction)
Tensile Strength	ISO 527-2	45 MPa	46 MPa	46 MPa
Elongation at Break	ISO 527-2	4.5%	4.5%	4%
Tensile Modulus	ISO 527-2	2800 MPa	2800 MPa	2800 MPa
Flexural Strength	ISO 178	67 MPa	67 MPa	58 MPa
Flexural Modulus	ISO 178	2100 MPa	2100 MPa	2000 MPa
Impact Strength / notched A	ISO 179-2	3.3 kJ/㎡	3.4 kJ/㎡	3.2 kJ/㎡
Unnotched Charpy Impact Strength	ISO 179-2	32 kJ/㎡	38 kJ/㎡	/
Shore Hardness D	ISO 868-2003	83.03 D	82.47 D	82.47 D
Heat Deflection Temp.@1.8 MPa	ISO 75-2	114°C	114°C	115°C

Powder Refresh Rate

See more details in Raise3D Powder Refresh Rate.

PA NEXT GB Black V1.0

Powder	Nitrogen Mode		Air Mode
Powder	Recommended or Not	Refresh Rate	Recommended or Not	Refresh Rate
PA NEXT GB Black V1.0	Recommended	30%	Printable	50%

Compare SLS Powder Properties

Compare the powder’s properties, and find the one that best meets your requirement.

Download Product Documents

TDS
SDS
RoHS
REACH
TSCA