Henkel LOCTITE 3D PRO410 Black 1kg
Benefits
- Excellent surface finish
- 3X faster printing*
- Accurate prototypes
*Values shown are linked to parts printed on a DLP printer at 385nm & post cured with broad spectra bulb (Loctite UVALOC 1000)
Ideal for
- Rapid prototypes
- Industrial
- Automotive
- Consumer goods
Material Properties*
*All specimen are printed unless otherwise noted. All specimen were in ambient lab conditions at 19-23°C / 40-60% RH for at least 24 hours. See more details in Technical Data Sheet.
| Testing Method | Green | Post-Processed | |
| Tensile Stress at Break |
ASTM D638 | 20-22 MPa | 38-49 MPa |
| Young’s Modulus | ASTM D638 | 703-883 MPa | 1630-1990 MPa |
| Elongation at Break |
ASTM D638 | 6-12% | 4-7% |
| Flexural Modulus | ASTM D790 | 781-937 MPa | 2480-2520 MPa |
| IZOD Impact (Notched) | ASTM D256 | N/A | 20-28 J/m |
| Heat Deflection Temp.@0.455 MPa | ASTM D648 | N/A | 66-76°C |