FFF • Dual Extrusion • High-Speed Printing up to 300mm/s • RFID Traceable Workflow
SLS • Low TCO • High Output • High-Precision Prints • Industrial and Functional Material
DLP • True DLP Precision • Faster Prints • RFID Traceable Workflow • Broad Resin Portfolio
DLP • High Resolution Resin Printing • RFID Traceable Workflow • Wide Range of Resin Compatibility
FFF • Dual IDEX • For Fiber-Reinforced Filaments • Dry Boxes • Enclosed Build Chamber
FFF • Dual IDEX • For Flexible Materials up to Shore Hardness 70A • Enclosed Build Chamber
Large-Format FFF (500 × 500 × 500 mm) • Dual IDEX • Carbon Fiber Composites & High-Strength Polymer
Stiffness & Thermal Durability
LOCTITE 3D IND249 is a high-temperature, high-strength material that prints challenging geometries with fine feature resolution. This low-viscosity material features exceptionally high green strength to enable ease of processing.
Stiffness and thermal durability make LOCTITE 3D IND249 ideal for production applications, including mold tooling, manufacturing aids, and other complex geometries.
*All specimen are printed unless otherwise noted. All specimen were conditioned in ambient lab conditions at 19-23°C / 40-60% RH for at least 24 hours. See more details in Technical Data Sheet.
| Testing Method | Green | Post-Processed | |
| Tensile Stress at Break |
ASTM D638 | 37 – 46 MPa | 83 – 98 MPa |
| Young’s Modulus | ASTM D638 | 1700 – 1880 MPa | 2980 – 3350 MPa |
| Elongation at Break |
ASTM D638 | 16 – 24% | 4 – 7% |
| Flexural Modulus | ASTM D790 | 2340 – 3330 MPa | 3170 – 3600 MPa |
| IZOD Impact (Notched) | ASTM D256 | 11 – 24 J/m | 13 – 24 J/m |
| Heat Deflection Temp.@0.455 MPa | ASTM D648 | N/A | 113 – 117°C |